Crystal Growth Blocking Strategy Enabling Efficient Solvent-Free Synthesis of Hierarchical UiO-66 for Large-Molecule Catalysis

Metal-organic frameworks (MOFs) with rich hierarchical structure have drawn great attention in the process with large molecule, such as catalysis and adsorption. However, efficiently and cost-effectively fabricating hierarchical MOFs with robust stability remains challenging. Herein, we report a crystal growth blocking strategy to prepare hierarchical UiO-66 by a solvent-free method. The addition of FeCl 3 in the synthetic system blocks the overgrowth of UiO-66 crystal and limits the particle size to around just 12 nm. After the removal of Fe by ethanol treatment, these small particles loosely aggregate and gain intercrystalline mesopores. The optimal sample Mes-UiO-66 exhibits well-developed hierarchical structure, the BET surface area reaches 1161.9 m 2 g -1 , and the mesopore volume attains a state-of-art 1.21 cm 3 g -1 . The superior catalytic performance and the robust stability of Mes-UiO-66 are demonstrated by the oxidation of DBT, of which the DBT conversion surpasses 99% and shows slight decrease after five cycles. Our finding may provide a novel platform for efficiently fabricating hierarchical MOFs for large molecule catalysis.